STRATA 888 For All Weldable Cast Iron

Enquire
Amazing electrode for repairing all cast iron
The high deposition rate of Strata 888 creates an extremely narrow heat affected zone. This feature is suitable for all weldable cast irons that require post weld machining. It is a one of a kind heavily copper clad "Tri-metal" cored cast iron electrode.
 

Key Features:

  • High efficiency weld metal transfer totally eliminates electrode overheating
  • Proprietary copper-nickel-iron deposit chemistry yields the ultimate combination of softness, ductility and tensile strength.
 

TYPICAL MECHANICAL PROPERTIES

Tensile Strength: 77,000 PSI (550 MPa)
Yield STrength: 54,000 PSI (380 MPa)
Elongation: 30%
Hardness: Rockwell B 84-88, Brinell 176, Vickers 185

Click Here to Download a pdf Product Specification Sheet

You might also be interested in ...

STRATA 845 For Non-Machineable Cast Iron

Special non-machineable, cast iron electrode for dirty heat-affect cast iron
Enquire for price

STRATA 885 Superior Strength for Cast Iron

For difficult position cast iron repairs with special no side arc characteristics
Enquire for price

STRATA 899 High Nickel Shallow Penetration

Very high nickel content providing ultimate machinability especially suitable for welding thin or eroded cast iron.
Enquire for price

STRATA 888 For All Weldable Cast Iron

Amazing electrode for repairing all cast iron
Enquire for price
GOT A WELDING CHALLENGE......?  Solve it with STRATA!  Btn Question
logo

STRATA INTERNATIONAL

0800 478 728
0800 4STRATA

sales@stratawelding.com

ABOUT US

STRATA International has been supplying welding electrodes to engineers throughout New Zealand for over 25 years and is pleased to support Proline Welding Supplies as the distributor for the South Pacific Region.
Trusted by many to weld in the most challenging applications, STRATA has proved itself to be 'better then the rest' when it comes to specialised welding products, a reputation not easily obtained, but strongly upheld.  Click here to read more.